This Article Full Text (PDF) Alert me when this article is cited Alert me if a correction is posted Services Similar articles in this journal Similar articles in PubMed Alert me to new issues of the journal Download to citation manager Reprints and Permissions Copyright Information Books from ASM Press MicrobeWorld Citing Articles Citing Articles via Google Scholar Google Scholar Articles by Lee, B. Articles by Bailey, T. B. Search for Related Content PubMed PubMed Citation Articles by Lee, B. Articles by Bailey, T. B., Jr. Agricola Articles by Lee, B. Articles by Bailey, T. B.

 Previous Article  |  Next Article 

Appl Environ Microbiol. 1991 March; 57(3): 678-685
Copyright © 1991, American Society for Microbiology. All Rights Reserved.

Biodegradation of Degradable Plastic Polyethylene by Phanerochaete and Streptomyces Species

¹ Department of Food Science and Human Nutrition and Center for Crops Utilization Research and Department of Statistics, ² Iowa State University, Ames, Iowa 50011

ABSTRACT

The ability of lignin-degrading microorganisms to attack degradable plastics was investigated in pure shake flask culture studies. The degradable plastic used in this study was produced commercially by using the Archer-Daniels-Midland POLYCLEAN masterbatch and contained pro-oxidant and 6% starch. The known lignin-degrading bacteria Streptomyces viridosporus T7A, S. badius 252, and S. setonii 75Vi2 and fungus Phanerochaete chrysosporium were used. Pro-oxidant activity was accelerated by placing a sheet of plastic into a drying oven at 70°C under atmospheric pressure and air for 0, 4, 8, 12, 16, or 20 days. The effect of 2-, 4-, and 8-week longwave UV irradiation at 365 nm on plastic biodegradability was also investigated. For shake flask cultures, plastics were chemically disinfected and incubated-shaken at 125 rpm at 37°C in 0.6% yeast extract medium (pH 7.1) for Streptomyces spp. and at 30°C for the fungus in 3% malt extract medium (pH 4.5) for 4 weeks along with an uninoculated control for each treatment. Weight loss data were inconclusive because of cell mass accumulation. For almost every 70°C heat-treated film, the Streptomyces spp. demonstrated a further reduction in percent elongation and polyethylene molecular weight average when compared with the corresponding uninoculated control. Significant (P < 0.05) reductions were demonstrated for the 4- and 8-day heat-treated films by all three bacteria. Heat-treated films incubated with P. chrysosporium consistently demonstrated higher percent elongation and molecular weight average than the corresponding uninoculated controls, but were lower than the corresponding zero controls (heat-treated films without 4-week incubation). The 2- and 4-week UV-treated films showed the greatest biodegradation by all three bacteria. Virtually no degradation by the fungus was observed. To our knowledge, this is the first report demonstrating bacterial degradation of these oxidized polyethylenes in pure culture.